英语翻译
介绍通过调整反应温度、反应时间、抗菌剂中银、锌离子的含量，研究载银锌沸石抗菌剂的稳定性和抗变色性，并对其抗变色性能和抗菌性能进行了测试和分析。得出载银锌沸石的最佳制备环境为使用0.1mol/L的AgNO3溶液和2mol/L的ZnSO4溶液进行混合在70℃的水浴锅中搅拌3小时。本文还采用抑菌环和抑菌率实验对最佳环境下制备载银锌沸石抗菌剂涂布抗菌包装纸的抗菌性能和物理性能进行了测定与研究。结果表明，减少载银锌沸石抗菌剂中银离子的含量，增加锌离子的含量，抗菌剂样品的抗菌性能变化不大，而抗变色性能却有较大提升。
使用该方法制备的载银锌沸石抗菌剂稳定性较好，避光保存时间较长，杀菌性能较好，抗变色性优良，是载银沸石的理想替代品。
关键词：抗菌材料；载银锌沸石；抑菌环测试；抗菌纸

Introduced by adjusting the reaction temperature, reaction time, antimicrobial agents silver and zinc ion content of antimicrobial silver zinc zeolite stability and anti-tarnish resistance, and its anti-tarnish properties and antibacterial properties were tested and analyzed. Silver zinc zeolite obtained the best preparation for the use of environment 0.1mol / L of the AgNO3 solution and 2mol / L of ZnSO4 solution was mixed in the mixing pot 70 ℃ water bath for 3 hours. This article also inhibitory rate by inhibition zone and the best experimental conditions for preparation of silver zinc coated zeolite antibacterial antibacterial agents antibacterial properties of wrapping paper and physical properties were determined and research. The results showed that the reduction of silver zeolite antimicrobial agent in the zinc content of silver ions to increase the zinc content of the antimicrobial properties of antimicrobial little change in the sample, and anti-tarnish performance there is much improvement.
Prepared using the method of antimicrobial silver zinc zeolite stability is good, dark storage time is longer, better bactericidal properties, excellent resistance to discoloration, silver zeolite is an ideal substitute.
Key words: antibacterial materials; containing silver-zinc zeolite; inhibition zone test; Antibacterial Pape